Best Price on Ceramic Saddles - Ceramic Berl Saddle Ring with 1″/1.5″/2″ – Kelley
Best Price on Ceramic Saddles - Ceramic Berl Saddle Ring with 1″/1.5″/2″ – Kelley Detail:
Application
Ceramic berl ring can be used in the drying towers, absorption towers, cooling towers, scrubbers and regeneration towers in the chemical metallurgy, gas and oxygen industries.
Technical Data
| SiO2 + Al2O3 | >92% | CaO | <1.0% |
| SiO2 | >76% | MgO | <0.5% |
| Al2O3 | >17% | K2O+Na2O | <3.5% |
| Fe2O3 | <1.0% | Other | <1% |
Physical & Chemical Properties
| Water absorption | <0.5% | Moh’s hardness | >6.5 scale |
| Porosity (%) | <1 | Acid resistance | >99.6% |
| Specific gravity | 2.3-2.40 g/cm3 | Alkali resistance | >85% |
| Firing temperature | 1280~1320℃ | Softening point | >1400℃ |
| Acid-resisting strength, %Wt. Loss (ASTMc279) | <4 | ||
Dimension And Other Physical Properties
|
Size |
Specific Surface |
Void Volume |
Number per |
Bulk Density |
|
|
(mm) |
(inch) |
(m2/m3) |
% | N/m3 | (Kg/m3) |
|
10 |
3/8 |
250 |
50 | 105000 |
950 |
|
15 |
3/5 |
225 |
58 |
83950 |
725 |
|
25 |
1 |
206 |
61 |
43250 |
640 |
|
38 |
1-1/2 |
110 |
72 |
12775 |
620 |
|
50 |
2 |
95 |
72 |
7900 |
650 |
Product detail pictures:
Related Product Guide:
Gaining client pleasure is our company's aim without end. We are going to make excellent efforts to create new and top-quality goods, meet your special requirements and provide you with pre-sale, on-sale and after-sale companies for Best Price on Ceramic Saddles - Ceramic Berl Saddle Ring with 1″/1.5″/2″ – Kelley, The product will supply to all over the world, such as: Oman, Mexico, Bhutan, We've got constantly insisted on the evolution of solutions, spent good funds and human resource in technological upgrading, and facilitate production improvement, meeting the wants of prospects from all countries and regions.
By Quintina from Stuttgart - 2018.08.12 12:27
This is a very professional and honest Chinese supplier, from now on we fell in love with the Chinese manufacturing.
By Rosalind from India - 2017.01.11 17:15